Resistance variable memory with temperature tolerant materials

ABSTRACT

A PCRAM memory device having a chalcogenide glass layer, preferably comprising antimony selenide having a stoichometric formula of about Sb 2 Se 3 , and a metal-chalcogenide layer and methods of forming such a memory device.

This is a divisional of U.S. patent application Ser. No. 10/916,423, filed on Aug. 12, 2004 now U.S. Pat. No. 7,365,411, the entirety of which is hereby incorporated by reference.

FIELD OF THE INVENTION

The invention relates to the field of random access memory (RAM) devices formed using a resistance variable material and a metal-chalcogenide material.

BACKGROUND

Resistance variable memory elements, which include Programmable Conductive Random Access Memory (PCRAM) elements, have been investigated for suitability as semi-volatile and non-volatile random access memory devices. In a typical PCRAM device, the conductivity/resistance of a chalcogenide glass backbone can be programmed to stable lower conductivity (i.e., higher resistance) and higher conductivity (i.e., lower resistance) states. An unprogrammed PCRAM device is normally in a lower conductivity, higher resistance state.

A conditioning operation forms a conducting channel of a metal-chalcogenide in the PCRAM device, which supports a conductive pathway for altering the conductivity/resistivity state of the device. After the conditioning operation, a write operation will program the PCRAM device to a higher conductivity state, in which metal ions accumulate along the conducting channel(s). The PCRAM device may be read by applying a voltage of a lesser magnitude than required to program it; the current or resistance across the memory device is sensed as higher or lower to define the logic “one” and “zero” states. The PCRAM may be erased by applying a reverse voltage (opposite bias) relative to the write voltage, which disrupts the conductive pathway, but typically leaves the conducting channel intact. In this way, such a device can function as a variable resistance memory having at least two conductivity states, which can define two respective logic states, i.e., at least a bit of data.

One exemplary PCRAM device uses a germanium selenide (i.e., Ge_(x)Se_(100-x)) chalcogenide glass as a backbone. The germanium selenide glass has, in the prior art, incorporated silver (Ag) by (photo or thermal) doping or co-deposition. Other exemplary PCRAM devices have done away with such doping or co-deposition by incorporating a metal-chalcogenide material as a layer of silver selenide (e.g., Ag₂Se), silver sulfide (AgS), or tin selenide (SnSe) in combination with a metal layer, proximate a chalcogenide glass layer, which during conditioning of the PCRAM provides material to form a conducting channel and a conductive pathway in the glass backbone.

Extensive research has been conducted to determine suitable materials and stoichiometries thereof for the glass backbone in PCRAM devices. Germanium selenide having a stoichiometry of about Ge₄₀Se₆₀, as opposed to Ge₂₃Se₇₇ or Ge₃₀Se₇₀, for example, has been found to function well for this purpose. A glass backbone of Ge₄₀Se₆₀, with an accompanying metal-chalcogenide (e.g., typically silver selenide) layer, enables a conducting channel to be formed in the glass backbone during conditioning, which can thereafter more easily be programmed to form a conductive pathway. The metal-chalcogenide is incorporated into chalcogenide glass layer at the conditioning step. Specifically, the conditioning step comprises applying a potential (e.g., about 0.20 V) across the memory element structure of the device such that metal-chalcogenide is incorporated into the chalcogenide glass layer, thereby forming a conducting channel within the chalcogenide glass layer. Movement of metal (e.g., typically silver) ions into or out of the conducting channel during subsequent writing and erasing forms or dissolves a conductive pathway along the conducting channel, which causes a detectible conductivity (or resistance) change across the memory device.

While germanium-chalcogenide (e.g., Ge₄₀Se₆₀) glass layers are highly desirable for some PCRAM devices, it may be desirable to use different chalcogenide glasses having different properties as a glass backbone.

SUMMARY

Exemplary embodiments of the invention provide a method of forming and a structure, in which a PCRAM memory device has a chalcogenide glass backbone layer, preferably comprising antimony selenide having a stoichometric formula of about Sb₂Se₃, and a metal-chalcogneide layer, which cooperates with the backbone layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 and 2 show exemplary embodiments of memory devices in accordance with the invention.

FIGS. 3-6 illustrate exemplary sequential stages of processing during the fabrication of an embodiment of the invention as shown in FIG. 1.

FIG. 7 shows an exemplary processor-based system incorporating memory devices in accordance with and embodiment the invention.

DETAILED DESCRIPTION

In the following detailed description, reference is made to various specific embodiments of the invention. These embodiments are described with sufficient detail to enable those skilled in the art to practice the invention. It is to be understood that other embodiments may be employed, and that various structural, logical, and electrical changes may be made without departing from the spirit or scope of the invention.

The term “substrate” used in the following description may include any supporting structure including, but not limited to, a semiconductor substrate that has a substrate surface. A semiconductor substrate should be understood to include silicon-on-insulator (SOI), silicon-on-sapphire (SOS), doped and undoped semiconductors, epitaxial layers of silicon supported by a base semiconductor foundation, and other semiconductor structures. When reference is made to a semiconductor substrate or wafer in the following description, previous process steps may have been utilized to form regions or junctions in or over the base semiconductor or foundation. The substrate need not be semiconductor-based, but may be any support structure suitable for supporting an integrated circuit, including, but not limited to, metals, alloys, glasses, polymers, ceramics, and any other supportive materials as is known in the art.

The term “chalcogenide glass” is intended to include glasses that comprise at least one non-chalcogenide component selected from Groups 3-15 and at least one chalcogenide component from Group 16 of the periodic table. Group 16 elements (e.g., sulfur (S), selenium (Se), tellurium (Te), polonium (Po), and oxygen (O)) are also referred to as chalcogens.

The term “metal-chalcogenide” is intended to include various alloys, compounds, and mixtures of metals and chalcogens (e.g., O, S, Se, Te, and Po), including some species which have a slight excess or deficit of metal. For example, tin selenide, a species of metal-chalcogenide, may be represented by the general formula SnSe, and silver selenide, another species of metal-chalcogenide, may be represented by the general formula Ag₂Se. The invention is not limited to a particular stoichiometric ratio between the metal and chalcogenide components. Also, the metal-chalcogenide preferably incorporates the same chalcogenide component as in the chalcogenide glass; however, this is not a requirement and it is possible for a different chalcogenide component to be used in the metal-chalcogenide.

The invention is now explained with reference to the figures, which illustrate exemplary embodiments and throughout which like reference numbers indicate like features. FIG. 1 shows an exemplary embodiment of a memory device 100 constructed in accordance with the invention. The device 100 shown in FIG. 1 is supported by a substrate 10. Over the substrate 10, though not necessarily directly so, is a conductive address line 12, which serves as an interconnect for the device 100 shown and a plurality of other similar devices of a portion of a memory array, of which the shown device 100 is a part. It is possible to incorporate an optional insulating layer (not shown) between the substrate 10 and address line 12, and this may be preferred if the substrate 10 is semiconductor-based. The conductive address line 12 can be any material known in the art as being useful for providing an interconnect line, such as doped polysilicon, silver (Ag), gold (Au), copper (Cu), tungsten (W), nickel (Ni), aluminum (Al), platinum (Pt), titanium (Ti), and other materials. Over the address line 12 is a first electrode 16, which is defined within an insulating layer 14, which is also over the address line 12. This electrode 16 can be any conductive material that will not migrate into chalcogenide glass, but is preferably tungsten (W). The insulating layer 14 should not allow the migration of metal (e.g., silver) ions and can be an insulating nitride, such as silicon nitride (Si₃N₄), a low dielectric constant material, an insulating glass, or an insulating polymer, but is not limited to such materials.

A memory element, i.e., the portion of the memory device 100 which stores information, is provided over the first electrode 16. In the embodiment shown in FIG. 1, a layer of chalcogenide glass 18, preferably antimony selenide having a stoichiometric formula of about Sb₂Se₃ (referred to hereafter as Sb₂Se₃ glass), is provided as a glass backbone over the first electrode 16. The layer of Sb₂Se₃ glass 18 is preferably between about 100 Å and about 1000 Å thick, most preferably about 150 Å thick. Layer 18 need not be a single layer of Sb₂Se₃ glass, but may also be comprised of multiple sub-layers of Sb₂Se₃ glass having the same or different stoichiometries. This layer of Sb₂Se₃ glass 18 is in electrical contact with the underlying electrode 16.

Over the Sb₂Se₃ glass layer 18 is a layer of metal-chalcogenide 20, preferably silver selenide (e.g., Ag₂Se). It is also possible that other metals may be substituted for silver, such as tin, and other chalcogenide materials may be substituted for selenium, such as sulfur, oxygen, or tellurium. The metal-chalcogenide layer 20 is preferably about 470 Å thick; however, its thickness depends, in part, on the thickness of the underlying Sb₂Se₃ glass layer 18. The ratio of the thickness of the metal-chalcogenide layer 20 to that of the underlying Sb₂Se₃ glass layer 18 should be between about 5:1 and about 1:1, more preferably about 2.5:1.

Still referring to FIG. 1, a metal layer 22 is provided over the metal-chalcogenide layer 20, with silver (Ag) or antimony (Sb) being preferred as the metal. This metal layer 22 should be about 200 Å thick. This metal layer 22 assists the switching operation of the memory device 100. Over the metal layer 22 is a second electrode 24. The second electrode 24 can be made of the same material as the first electrode 16, but is not required to be so. In the exemplary embodiment shown in FIG. 1, the second electrode 24 is preferably tungsten (W). The device(s) may be isolated by an insulating layer 26.

Devices constructed according to the embodiments of the invention, particularly those having a Sb₂Se₃ layer (e.g., glass backbone layer 18) show improved temperature tolerance relative to PCRAM devices using a germanium selenide glass backbone.

FIG. 2 shows another exemplary embodiment of a memory device 101 constructed in accordance with the invention. Memory device 101 has many similarities to memory device 100 of FIG. 1 and layers designated with like reference numbers, such as Sb₂Se₃ glass layer 18, are preferably the same materials and have the same thicknesses as those described in relation to the embodiment shown in FIG. 1. The primary difference between device 100 and device 101 is the addition to device 101 of optional chalcogenide glass layers 18 a and 18 b.

The optional chalcogenide glass layer 18 a is formed over the metal-chalcogenide layer 20, is preferably Ge₄₀Se₆₀, and is preferably about 150 Å thick. Over this optional chalcogenide glass layer 18 a is a metal layer 22, which is preferably silver (Ag) or antimony (Sb) and is preferably about 200 Å thick. Over the metal layer 22 is another optional chalcogenide glass layer 18 b, which is preferably Ge₄₀Se₆₀ and is preferably about 100 Å thick. The optional chalcogenide glass layer 18 b provides an adhesion layer for subsequent electrode formation. As with layer 18 of FIG. 1, layers 18 a and 18 b are not necessarily a single layer, but may be comprised of multiple sub-layers. Additionally, the optional chalcogenide layers 18 a and 18 b may be the same as or different chalcogenide glasses from the antimony selenide glass layer 18 or each other. Other chalcogenide glasses that may be useful for this purpose include, but are not limited to, germanium sulfide (GeS), and combination of germanium (Ge), silver (Ag), and selenium (Se).

Over the optional chalcogenide glass layer 18 b is a second electrode 24, which may be any conductive material, except those that will migrate into the stack and alter memory operation (e.g., Cu or Ag), as discussed above for the preceding embodiments. Preferably, the second electrode 24 is tungsten (W).

The above-discussed embodiments are exemplary embodiments of the invention utilizing a Sb₂Se₃ glass backbone layer (e.g., layer 18); however, other exemplary embodiments may be used which combine the first electrode layer 16 and address line layer 12. Another exemplary embodiment may use blanket layers (e.g., layers 16, 18, 20, and 22 of FIG. 1) of the memory cell body, where the memory cell is defined locally by the position of the second electrode 24 over the substrate 10. Another exemplary embodiment may form the memory device within a via. Additional layers, such as barrier layers or alloy-controlling layers, not specifically disclosed in the embodiments shown and discussed above, may be added to the devices in accordance with the invention without departing from the scope thereof.

FIGS. 3-6 illustrate a cross-sectional view of a wafer during the fabrication of a memory device 100 incorporating a Sb₂Se₃ glass backbone layer, as shown by FIG. 1. Although the processing steps shown in FIGS. 3-6 most specifically refer to memory device 100 of FIG. 1, the methods and techniques discussed may also be used to fabricate memory device 101 of FIG. 2, or other embodiments, as would be understood by a person of ordinary skill in the art based on a reading of this specification.

As shown by FIG. 3, a substrate 10 is provided. As indicated above, the substrate 10 can be semiconductor-based or another material useful as a supporting structure as is known in the art. If desired, an optional insulating layer (not shown) may be formed over the substrate 10; the optional insulating layer may be silicon nitride or other insulating materials used in the art. Over the substrate 10 (or optional insulating layer, if desired), a conductive address line 12 is formed by depositing a conductive material, such as doped polysilicon, aluminum, platinum, silver, gold, nickel, but preferably tungsten, patterning one or more conductive lines, for instance with photolithographic techniques, and etching to define the address line 12. The conductive material maybe deposited by any technique known in the art, such as sputtering, chemical vapor deposition, plasma enhanced chemical vapor deposition, evaporation, or plating.

Still referring to FIG. 3, over the address line 12 is formed an insulating layer 14. This layer 14 can be silicon nitride, a low dielectric constant material, or many other insulators known in the art that do not allow metal (e.g., silver) ion migration, and may be deposited by any method known in the art. An opening 14 a in the insulating layer is made, for instance by photolithographic and etching techniques, thereby exposing a portion of the underlying address line 12. Over the insulating layer 14, within the opening 14 a, and over the address line 12 is formed a conductive material, preferably tungsten (W). A chemical mechanical polishing step may then be utilized to remove the conductive material from over the insulating layer 14, to leave it as a first electrode 16 over the address line 12, and planarize the wafer.

FIG. 4 shows the cross-section of the wafer of FIG. 3 at a subsequent stage of processing. A series of layers making up the memory device 100 (FIG. 1) are blanket-deposited over the wafer. A Sb₂Se₃ glass layer 18 is formed to a preferred thickness of about 150 Å over the first electrode 16 and insulating layer 14. Deposition of this Sb₂Se₃ glass layer 18 may be accomplished by any suitable method, such as evaporative techniques or chemical vapor deposition; however, the preferred technique utilizes either sputtering from an antimony selenide target having the desired stoichiometry or co-sputtering antimony and selenium in the appropriate ratios.

Still referring to FIG. 4, a metal-chalcogenide layer 20 is formed over the Sb₂Se₃ glass layer 18. The metal-chalcogenide layer 20 is preferably silver selenide (e.g., Ag₂Se), but may be other metal-chalcogenide combinations as well. Physical vapor deposition, chemical vapor deposition, co-evaporation, sputtering, or other techniques known in the art may be used to deposit layer 20 to a preferred thickness of about 470 Å. Again, the thickness of layer 20 is selected based, in part, on the thickness of Sb₂Se₃ layer 18 and the ratio of the thickness of the metal-chalcogenide layer 20 to that of the underlying Sb₂Se₃ glass layer 18 is preferably from about 5:1 to about 1:1, more preferably about 2.5:1. It should be noted that, as the processing steps outlined in relation to FIGS. 3-6 may be adapted for the formation of devices in accordance with alternative embodiments of the invention having an alloy-control layer or a barrier layer formed adjacent to the metal-chalcogenide layer 20, on either side thereof.

Still referring to FIG. 4, a metal layer 22 is formed over the metal-chalcogenide layer 20. The metal layer 22 is preferably silver (Ag) or antimony (Sb), or at least contains silver or antimony, and is formed to a preferred thickness of about 200 Å. The metal layer 22 may be deposited by any technique known in the art.

Still referring to FIG. 4, over the metal layer 22, a conductive material is deposited for a second electrode 24. Again, this conductive material may be any material suitable for a conductive electrode, but is preferably tungsten; however other materials may be used such as titanium nitride or tantalum, for example.

Now referring to FIG. 5, a layer of photoresist 30 is deposited over the top electrode 24 layer, masked and patterned to define the stacks for the memory device 100, which is but one of a plurality of like memory devices of a memory array. An etching step is used to remove portions of layers 18, 20, 22, and 24, with the insulating layer 14 used as an etch stop, leaving stacks as shown in FIG. 13. Then, the photoresist 30 is removed, leaving a substantially complete memory device 100, as shown by FIG. 6. An insulating layer 26 may be formed over the device 100 to achieve a structure as shown by FIG. 1. This isolation step can be followed by the forming of connections to other circuitry of the integrated circuit (e.g., logic circuitry, sense amplifiers, etc.) of which the memory device 100 is a part, as is known in the art.

A conditioning step is performed by applying a voltage of about 0.20 V across the memory element to incorporate material from the metal-chalcogenide layer 20 into the Sb₂Se₃ glass layer 18 to form a conducting channel in the glass layer 18. The conducting channel will support a conductive pathway during memory function of the memory device 100. The formation and disruption of the conductive pathway by writing or erasing the memory device 100 provides the logic one and zero for memory function.

The embodiments described above refer to the formation of only a few possible resistance variable memory device structures (e.g., PCRAM) in accordance with the invention, which may be part of a memory array. It must be understood, however, that the invention contemplates the formation of other memory structures within the spirit of the invention, which can be fabricated as a memory array and operated with memory element access circuits.

FIG. 7 illustrates a typical processor system 400 which includes a memory circuit 448, e.g., a PCRAM device, which employs resistance variable memory devices (e.g., device 100 or 101) fabricated in accordance with the invention. A processor system, such as a computer system, generally comprises a central processing unit (CPU) 444, such as a microprocessor, a digital signal processor, or other programmable digital logic devices, which communicates with an input/output (I/O) device 446 over a bus 452. The memory circuit 448 communicates with the CPU 444 over bus 452 typically through a memory controller.

In the case of a computer system, the processor system may include peripheral devices such as a floppy disk drive 454 and a compact disc (CD) ROM drive 456, which also communicate with CPU 444 over the bus 452. Memory circuit 448 is preferably constructed as an integrated circuit, which includes one or more resistance variable memory devices, e.g., device 100. If desired, the memory circuit 448 may be combined with the processor, for example CPU 444, in a single integrated circuit.

The above description and drawings should only be considered illustrative of exemplary embodiments that achieve the features and advantages of the invention. Modification and substitutions to specific process conditions and structures can be made without departing from the spirit and scope of the invention. Accordingly, the invention is not to be considered as being limited by the foregoing description and drawings, but is only limited by the scope of the appended claims. 

1. A memory device comprising: a first electrode; a second electrode; a Sb₂Se₃ glass layer between said first electrode and said second electrode; a metal-chalcogenide layer between said Sb₂Se₃ glass layer and said second electrode, a first chalcogenide glass layer between said metal-chalcogenide layer and said second electrode; a metal-containing layer between said first chalcogenide glass layer and said second electrode; and a second chalcogenide glass layer between said metal-containing layer and said second electrode.
 2. The memory device of claim 1, wherein said metal-chalcogenide layer comprises Ag₂Se, wherein said first chalcogenide glass layer and said second chalcogenide glass layer, comprise Ge₄₀Se₆₀, and wherein said metal-containing layer comprises at least one of silver and antimony.
 3. A memory device, comprising: a substrate; a conductive address line over said substrate; a first electrode over said conductive address line; a Sb₂Se₃ glass layer over said first electrode; a metal-chalcogenide layer over said Sb₂Se₃ glass layer; a first chalcogenide glass layer over said metal-chalcogenide layer; a metal layer over said first chalcogenide glass layer; a second chalcogenide glass layer over said metal layer; and a second electrode over said second chalcogenide glass layer.
 4. The memory device of claim 3, wherein said first electrode comprises tungsten.
 5. The memory device of claim 3, wherein said second electrode comprises tungsten.
 6. The memory device of claim 3, wherein said metal-chalcogenide layer comprises tin selenide.
 7. The memory device of claim 3, wherein said metal-chalcogenide layer comprises silver selenide.
 8. The memory device of claim 3, wherein said metal-chalcogenide layer comprises Ag₂Se, wherein said first chalcogenide glass layer and said second chalcogenide glass layer, comprise Ge₄₀Se₆₀, and wherein said metal-containing layer comprises at least one of antimony and silver.
 9. The memory device of claim 3, wherein said Sb₂Se₃ glass layer, said metal-chalcogenide layer, said first and second chalcogenide layer, said metal layer, and said second electrode are provided within a via.
 10. The memory device of claim 3, wherein said second electrode defines the location of said memory device over said substrate.
 11. The memory device of claim 3, wherein said memory device is a PCRAM device.
 12. The memory device of claim 3, wherein said Sb2Se3 glass layer has a conducting channel therein.
 13. The memory device of claim 3, wherein said conducting channel comprises material from said metal-chalcogenide layer.
 14. The memory device of claim 3, wherein a conductive pathway within said Sb₂Se₃ glass layer provides a higher conductivity memory state for said memory device.
 15. The memory device of claim 14, wherein said conductive pathway comprises silver. 